Zn1-x Cox O (0≤ x≤ 0.10) nano-particles were fabricated successfully via ball milling procedure. The influence of [Co]/[Zn] on the properties of nano-particles was examined employing X-ray diffraction, the energy dispersion of the X-ray (EDX), Scan Electron Microscope (SEM), these measurements exhibit the growth hexagonal wurtzite crystal phase Zn<sub>1-x</sub>Co<sub>x</sub>O nano-particles with the successfully incorporation of Co<sup>+2</sup> ions in the ZnO lattice. The optical characterization investigated utilizing Ultraviolet-Visible (UV) absorption spectroscopy for Zn<sub>1-x</sub>Co<sub>x</sub>O nano-particles refers to a red-shift in the optical bandgap with increasing Co ion inside ZnO matrix, this result confirm the bandgap is considerably narrowed with increasing Co ratio. The measurements of magnetization applying vibrating sample magnetometer illustrated a hysteresis loop in Co-doped ZnO nano-particles. Thanks to the variation values of bandgap E<sub>g</sub><sup>opt</sup> and magnetic measurements of ZnO nano-particles doped Co% plays a major role for selective coatings of optoelectronics; use as antireflective coating materials, and fabrication of optoelectronic devices.
ملخص البحث
قسم البحث
مجلة البحث
Journal of Ovonic research
المشارك في البحث
عدد البحث
17
سنة البحث
2021