It is well established that aluminum and its alloys are industrially grain refined by adding either Ti or Ti-B to improve their mechanical behavior and surface finish. In a previous paper, it was found that the grain refining efficiency of aluminum master alloys containing Ti or Ti+B was enhanced by addition of small amounts of other elements including vanadium. V. Therefore, it is anticipated that such an element will improve mechanical behavior, machinability and wear resistance of aluminum and its alloys. In this paper, the effect of vanadium addition, up to 0.3% on mechanical behavior is investigated. Machinability was assessed under different cutting conditions: speed, feed and depth of cut and finally the wear resistance was determined at different loads and speeds. The results indicated that improvement in hardness and mechanical strength were achieved by the addition of V that addition of more than 0.2%V resulted in little or no improvement. Similarly, addition of V resulted in improvement of surface quality under the different cutting conditions of speed, feed and depth of cut, and resistance to wear. However addition of more than 0.2% V resulted in increase of wear rate and change of wear mechanisms.