The use of corrosion inhibitors is considered as the supreme dominant approach to control the damage of metallic corrosion. Organic dyes are extensively employed as inhibitors for the corrosion of various metals and alloys in diverse media. Herewith, Alcian blue dye (ABD) was selected to investigate its inhibitive characteristics against the corrosion of copper in 1.0 M H2SO4 solution at 298 K. This investigation was monitored by various chemical, electrochemical, and spectroscopic techniques. The results indicated that the examined dye is a proficient inhibitor for the corrosion of copper in 1.0 M H2SO4 solution and its inhibition efficiency (% IE) was increased with augmenting its concentration and diminished with rising medium temperature. The high anticorrosive ability of the selected dye was attributed to its adherent adsorption of such dye on the Cu surface and follows Langmuir isotherm. Thermodynamics and kinetics of corrosion of copper and its inhibition by the examined dye were inspected. The mechanisms of copper corrosion in H2SO4 solution and its inhibition by ABD were proposed. The obtained results illuminated that the examined dye acts as a mixed-type inhibitor with cathodic precedence. Finally, all gained results with respect to % IE values of the dye were compared and designated a good harmony between all applied techniques.