Synthesis, Characterization and Corrosion Inhibitive Properties of NewThiazole Based Polyamides Containing Diarylidenecyclohexanone Moiety

Research Authors
K.I. Aly and M.A. Hussein
Research Abstract

The present work aimed to synthesize a new interesting series of thiazole based polyamides containing
diarylidenecyclohexanone moiety 5a−5f using low temperature solution polycondensation technique. The new polymers were
synthesized by the reaction of thiazole based monomer namely, bis(2-aminothiazol-4-ylbenzylidene)cyclohexanone 3 with
different aliphatic and aromatic diacid chlorides using NMP, and in the presence of anhydrous LiCl as catalyst. Adipoyl,
sebacoyl, oxaloyl, terephthaloyl, isophthaloyl dichlorides and biphenyl dicarbonyl dichloride were used as diacid chlorides.
The structure of the model compound 4 as well as the new polymers was confirmed by correct elemental and spectral
analyses. The thermal properties of those polymers were evaluated by TGA and DTG measurements and correlated to their
structural units, beside X-ray diffraction analysis, solubility and viscometry measurements. The inherent viscosities for the
synthesized polymers were in the range 0.6–1.03 dL/g. On the other hand the corrosion inhibitive properties of monomer 3 as
well as polyamides 5d and 5f as selected examples were carried out on carbon-steel in 0.5 mol/L H2SO4 at 40 °C. The
calculated inhibition efficiency (IE%) for polymer 5d was in the range (82 ± 6)% in all selected concentrations. The best
value of IE% was obtained at 1 mg/L to reach 98.24% for polymer 5d and at 0.5 mg/L to reach 87.75% for polymer 5f.